Forums > Windsurfing Tasmania

Relic Repair

Reply
Created by Relic > 9 months ago, 7 Oct 2016
nickpryde
TAS, 189 posts
31 Oct 2016 9:59PM
Thumbs Up

yea, it makes sense that the tension load is probably on the bottom... but i have a bad feeling...

nickpryde
TAS, 189 posts
31 Oct 2016 10:03PM
Thumbs Up

relic seems a pro at this stuff,
there is a pretty interesting site: boardlady.com/
for anyone who is interested in more tutes



geared4knots
TAS, 2645 posts
31 Oct 2016 10:18PM
Thumbs Up

Yeah board lady does it for me.
That rocks! I remember using her tips over 15 years ago.

windsurftom
NSW, 332 posts
1 Nov 2016 5:54AM
Thumbs Up

Great thread relic.

You got a great looking result on that innegra rail!

Relic
TAS, 837 posts
1 Nov 2016 7:13AM
Thumbs Up

A fellow windsurfer with far more repair and knowledge on the topic of forces on boards has provided a much more detailed correct explaination.
I thought it too valuable not to share with everyone. I stand corrected.
I have drawn a lot from Eva Hollymans's site, with over 5000 repairs and vast knowledge as a naval architect she is the guru. Often unfairly maligned. She is also very generous having replied to an email I sent her regarding a technical question.
I'm happy with the interest shown with the thread. I hope it will enable those inclined like me to repair their own boards. Having to pay for this type of stuff is bloody expensive. I'm no genius. If I can do it anyone can. Power to the Internet for enabling the sharing of knowledge. However as a clever bloke famously said; "Imagination is far more important than knowledge"


Hi Paul. as you are aware there are lots of forces acting on a board when under normal sailing conditions. In a failure situation (the more common one of many) due to high impact landing, it is the bottom that that is put under compression and the deck is under tension. When landing flat or onto a bit chop, there are 2 downward forces. That of the mast rig with some of your upper weight on it and the other being the resultant weight you place through the footstrap area. Opposing these forces is the flat section landing between the mast track and footstraps. This results in the bottom bending around that landing area and becoming under compression; the deck is therefore placed under tension through that area.
Looking at the bottom layup it is the outer glass that is under compression and the inner glass that is under tension. It is normally that outer glass that delaminates first as it buckles under compression and the forces directly applied from the fluid. From that point, if the loading is great enough the pvc will buckle and fold back into the EPS creating a crease along the bottom, this may tear the pvc and layers if the board springs back fast and adds tension to the already delaminated outer layer(bottom crease). looking at the top, if the loading is that great and the bottom holds for that split longer then the tensile forces on the deck will first cause the deck inner layer to delaminate as it buckles under compression, followed by the pvc buckling and in turn the carbon or glass etc. outer layer will tear apart from tensile and shear forces and the board will snap from deck down. There are other scenarios but this is the most common
So under common fault conditions(most of our landings) the deck is under tension, but not forgetting that the actual deck sandwich although in total tension; the inner layer is also under compression from bending forces.

Flouro1
WA, 991 posts
1 Nov 2016 4:45AM
Thumbs Up

Arrr the eternal search for performance (weight) vs strength (durability) and cost .

Relic
TAS, 837 posts
2 Nov 2016 8:01AM
Thumbs Up

Select to expand quote
windsurftom said..
Great thread relic.

You got a great looking result on that innegra rail!


Thanks...with a bit more time & effort a near invisible result is possible. I wanted to finish fast as the first good seabreeze at one of our favourite breaks was beckoning. Besides board is generally tatty but water tight never having been used with damage taped up. The visible repairs are badges of hounour in my book and make for good stories.
Don't think tape will keep water out. It will not! I always carry a ding stick in the car and pack damage extending the temporary repair over unbroken skin. I reckon keeps more moisture out till a proper repair is done. A few $for a ding stick is worth not having a soggy mess that will take a long time to dry out.

Importantly, I forgot to mention; if a repair is not being painted UV stable resin is a must. Normal resin will turn yellow very quickly.

nickpryde
TAS, 189 posts
2 Nov 2016 7:01PM
Thumbs Up

in other news... for sale is my starboard acid wave board... these were awesome boards back in the day and great for high wind blasting too.

its 66 l, so its good for the big days...

pete stevenson wrinkled the deck doing one of his massive delayed forwards.

i fixed the deck, turns out that the thai dude on a dollar a day, left a massive area of dry glass in the deck so arguably this ones stronger than new...(had trouble matching the grip deck as you can see...)

its never been sailed since...so buyer be ware, very aware


Relic
TAS, 837 posts
2 Nov 2016 8:52PM
Thumbs Up

I reckon the resin goes off in the heat before the dudes get the glass wet out. Or they have a ration per board!

R1DER
WA, 1455 posts
2 Nov 2016 10:24PM
Thumbs Up

Hey great thread Relic. I can live vicariously through you in the comfort of my lounge room without getting itchy. Plus I have a list of domestic jobs to do around the house and garden putting a hold on my own board tweaking.
Nice rail repair and doing those strips on the deck was a very clever idea

Re boards breaking I put a post on the boards forum as there are quite a few clever board tweaker on there including shapers for Witchcraft and Simmer boards http://forums.boards.co.uk/showthread.php/77318-How-does-a-board-break-or-crease#fSThZ8dOdCRS0ok8.97

Ps your vacuum pump looks so neat and professional very impressive!

Looking forward to seeing more of your project.

Relic
TAS, 837 posts
3 Nov 2016 6:39AM
Thumbs Up

R1DER said..
Hey great thread Relic. I can live vicariously through you in the comfort of my lounge room without getting itchy. Plus I have a list of domestic jobs to do around the house and garden putting a hold on my own board tweaking.
Nice rail repair and doing those strips on the deck was a very clever idea

Re boards breaking I put a post on the boards forum as there are quite a few clever board tweaker on there including shapers for Witchcraft and Simmer boards http://forums.boards.co.uk/showthread.php/77318-How-does-a-board-break-or-crease#fSThZ8dOdCRS0ok8.97

Ps your vacuum pump looks so neat and professional very impressive!

Looking forward to seeing more of your project.


Coming from you Mike, that's a big compliment. Mundane things are slowing me a little too. However the interruptions have given time to come up with some "Outside the box" ideas like the strips. I've used a West System epoxy resin glue for a long time to repair nearly anything. The bond achieved is amazingly strong. I'm going to seam glue the fracture line, cut small slots with a cut off grinder wheel perpendicular to the fracture and glue it Before the top layer of carbon goes on. The idea being to try and eliminate the straight line of weakness across the board.
The weight gain is around 1/2kg at this stage. Cost too is a consideration. It's running at about $250. Is it worth It? Considering the educational value with the end game being a board build I think yes. Not forgetting an extra board too....if it stays in one piece! It will be renamed; "Snapp 92"
The pump's ok. It looks the business but I'm not sure if I'm getting enough vacuum. Hard to know because it's my first experience vaccing. I also have to be neat because my shed is tiny; 3x3m only barely enough room to squeeze around a board on the "Operating Table"

R1DER
WA, 1455 posts
3 Nov 2016 7:42AM
Thumbs Up

Your gauge shows your getting enough vacuum, I think they're just slow as its so low in volume, a mate with no gauge using a fridge compressor managed to change his vee from 4mm each side to 25mm by mistake on a board he was making. I was wondering how you were going to tackle the rest of the crack. I think it'll be stronger than when first made.

Gclark1
TAS, 546 posts
3 Nov 2016 3:36PM
Thumbs Up

Surely the LEARNER (no names) is going to foot the bill, so it's all FREE anyway...

I am still contemplating putting twin boxes in my 66 Evo. I rode it on the weekend after being on my 74 Evil Twin for the last few weeks and you just can't 'slam' the single fin board into a turn, but if you could, it would be the best board on the planet - hands down.

So, anyone who wants to supplement the Relic Repair Shop - On-Line, with hot tips on fitting boxes...feel free! The low tech 'tools-you-happen-to-have-lying-around-anyway' version would be good.

Are there CPD points in this?

robdddd
TAS, 167 posts
3 Nov 2016 4:04PM
Thumbs Up

CPD argument :....familiarization with alternative materials to assess their suitability for implementation into custom architectural forms...... blah blah blah!

Relic
TAS, 837 posts
3 Nov 2016 5:51PM
Thumbs Up

Select to expand quote
Gclark1 said..
Surely the LEARNER (no names) is going to foot the bill, so it's all FREE anyway...

I am still contemplating putting twin boxes in my 66 Evo. I rode it on the weekend after being on my 74 Evil Twin for the last few weeks and you just can't 'slam' the single fin board into a turn, but if you could, it would be the best board on the planet - hands down.

So, anyone who wants to supplement the Relic Repair Shop - On-Line, with hot tips on fitting boxes...feel free! The low tech 'tools-you-happen-to-have-lying-around-anyway' version would be good.

Are there CPD points in this?




I'll whack 'em in for you Clarky. I owe you for the two kids boards!

Relic
TAS, 837 posts
4 Nov 2016 10:32AM
Thumbs Up

Put carbon fibre strands in the slots
















nickpryde
TAS, 189 posts
4 Nov 2016 10:11PM
Thumbs Up

i wonder if your carbon inlays would be better pre-tensioned...

nickpryde
TAS, 189 posts
4 Nov 2016 10:38PM
Thumbs Up

re pump,
somewhere i have read a guide on vac pressure to use. i can get -.8 bar and that will suck the resin out of your job...

I can't remember what vac pressure you need but .25-.3 rings a bell but i wouldn't take my own word on this one...

nickpryde
TAS, 189 posts
4 Nov 2016 10:47PM
Thumbs Up

do you have a needle value in vac pump line? it allows you to adjust your pressure...

Relic
TAS, 837 posts
5 Nov 2016 6:52AM
Thumbs Up

Select to expand quote
nickpryde said..
re pump,
somewhere i have read a guide on vac pressure to use. i can get -.8 bar and that will suck the resin out of your job...

I can't remember what vac pressure you need but .25-.3 rings a bell but i wouldn't take my own word on this one...

Thanks Nick, the feedback is appreciated. I'm getting as much info back from everyone as I'm giving. Keep it coming. info on lay ups would be great too. Although some are a bit secretive The link Rider1 put up on discussion of board stresses is worth a read.
The gate valve on the olier controls the vacum. It's crude but it works.
In hindsight I think there was enough vacuum; -30-40 kPa, because the PVC layer sucked down into the core about 1 mm too much. Initially I thought I had got the cut out depth wrong. I'm pretty sure it was correct because I did test cuts before the big chop out.
.....Now getting the carbon strands under tension would be a challenge. Putting them in was just to give the glue more structure. It probably wasn't necessary as the glue sets bloody hard. I had the leftovers so why not use them. It can't do any harm. It also gave me the opportunity to shove some glue between the core and composite. Every little bit helps

Relic
TAS, 837 posts
5 Nov 2016 9:49AM
Thumbs Up

Decided to glue finger strips after doing the first as a test. Peel ply & plastic over the top and taped tight.

Used up the remaining carbon fibre strands

Uni bias strips over PVC Opposite to bottom. Assuming deck is under tension during hard landing.






I'm starting to think it will be strong...

Relic
TAS, 837 posts
5 Nov 2016 8:08PM
Thumbs Up

Result revealed with peel ply off exceeded expectations. The Epoxy resin glue has filled all the voids. With the bond this stuff achieves it should be bombproof. Well worth 100g more weight.

A quick sand and top layer of carbon fibre double bias cloth will complete structural work.



John340
QLD, 3047 posts
8 Nov 2016 11:07AM
Thumbs Up

Relic,
Fantastic work, I'm really enjoying the post. One question, did you consider removing and replacing the sandwich construction on the top deck, 300 mm either side of the break, in lieu of the carbon fingers and single carbon layer?

Relic
TAS, 837 posts
8 Nov 2016 12:18PM
Thumbs Up

Considered

Select to expand quote
John340 said..
Relic,
Fantastic work, I'm really enjoying the post. One question, did you consider removing and replacing the sandwich construction on the top deck, 300 mm either side of the break, in lieu of the carbon fingers and single carbon layer?



Yes considered that. Decision not to was: A lot of work and deck skin not delaminated. I've just applied the final lay up;
The area to be glassed was cross etched with a grinder cut off wheel and sanded with 60 Grade to expose top layer of original glass to get a good "Key" bond as well as even up the "Fingers".

As a result of too much vacum on the bottom the composite sucked into the core slightly. Rather than just use filler left over single bias and strips of mat have been glassed in to get some rail strength back.

The deck has had a layer of CF double bias layed over from 200mm in front of mast track to behind front heel position.



Vent and track masked out to stop getting full of resin. Unlikely but a precaution. Foot strap holes have been countersunk hopefully to leave indentations in the top layer to bee re-drilled. (Thanks for the idea Rider1)



Relic
TAS, 837 posts
8 Nov 2016 7:09PM
Thumbs Up

Glassing all done

Extra glass on rails has filled the indents. Top layer is wrapped around to bottom.


Holes located and drilled before filler is applied.


R1DER
WA, 1455 posts
11 Nov 2016 9:07PM
Thumbs Up

Looking good.

I think any vac pressure will compress the eps and cause it to sink a bit, my repair sunk .5mm I think it happens even when making a board but it doesn't get noticed cause its the whole bottom.

Relic
TAS, 837 posts
13 Nov 2016 1:33PM
Thumbs Up

Second coat of filler on after first was sanded.

Restoring the rail shape was much easier and successful than previous repairs where I cut out and rebuilt around the fracture. Remains to be seen if it's strong enough.








Relic
TAS, 837 posts
19 Nov 2016 6:14PM
Thumbs Up

Done.....can anyone lend me some fins and straps. Im broke after the repair













Gclark1
TAS, 546 posts
21 Nov 2016 7:58AM
Thumbs Up

Chalk and Cheese!

The original board drove a Volvo, wore a hat, never swore, ate its greens, was teetotal, well mannered and generally reserved. Kind of beige...

The new board - even when it is NOT busting a move it will look like it is anyway (might need to get me one of these...)

I am thinking "Darth Sith"

Flouro1
WA, 991 posts
22 Nov 2016 5:34AM
Thumbs Up

Hi tect Hawaii waveboard graphics from the late 80's cool retro look
Always wanted one of those zebra patterned wave boards might get the starboard resprayed



Subscribe
Reply

Forums > Windsurfing Tasmania


"Relic Repair" started by Relic